On Thermal Insulation Properties of Various Foaming Materials Modified Fly Ash Based Geopolymers

Geopolymers can be used as a thermally insulated material because of their considerable porosity, whereas the combined effect of various modifying agents on their heat-insulating properties remains unexplored. Here, orthogonal experiments were carried out to evaluate the thermal insulation performance of fly ash geopolymer modified by phenolic resin, silica aerogel, and hydrogen peroxide. Moreover, variance analysis and range analysis were applied to estimate the influence of modifying agents on the thermal insulation performance of the geopolymer. The results demonstrate that the thermal conductivity of fly ash geopolymer significantly reduces (from 0.48 W/m·K to 0.12 W/m·K) due to the combined effect of the three modifying agents. Based on the variance analysis and range analysis, the optimum thermal conductivity ultimately reaches 0.08 W/m·K via a best composition scheme of the three modifying agents. Moreover, phenolic resin can facilitate the formation of a network structure and increase the porosity of micron pores (>1 μm). Hydrogen peroxide can be decomposed into O₂ in an alkaline environment and leave large-diameter pores (>1 μm) during curing. Some silica aerogel is embedded in the geopolymer matrix as microspheres with extremely low thermal conductivity, whereas the rest of the silica aerogel may react with the alkali activator to form water, and subsequently leaves pores (>1 μm) after evaporation of water during the curing. In addition, a newly modified Maxwell-Euchen model using iterative calculation and considering the Knudsen effect (pores of micron or even nanometer scale) is proposed and validated by the experimental data. The foamed geopolymer in this research can be used as a reference for building insulation layer design. This research unravels phenolic resin-, silica aerogel-, and hydrogen peroxide-influenced thermal insulation mechanisms of geopolymer that may have impacts on deployment of a thermally insulating material in the construction field.