Thermodynamic analysis and application for extracting valuable components from iron-phosphorus residue of spent...

The method of extracting valuable metals from spent catalysts has been developed in recent years. In this paper, the solid waste produced in the treatment of spent catalyst was studied and named iron-phosphorus residue (IPR). IPR was composed of FePO₄·2H₂O, Fe₃(PO₄)₂·3H₂O, Fe₅(PO₄)₄(OH)₃·2H₂O, and SiO₂. Appreciable quantities of Ni, Co, V, Mo, and W were detected in IPR. Based on E-pH diagrams, different atmospheric leaching strategies were used to extract valuable components from IPR. Both the HCl and NaOH leaching are appropriate for treating IPR. An in-depth investigation on HCl atmospheric leaching showed that >95% of Fe, Ni, Co, V, and Mo, 76.9% of W, and 89.3% of P were extracted efficiently and SiO₂ was enriched into the leach residue, at leaching temperature of 90 ℃, leaching time of 180 min, initial HCl concentration of 5 mol/L and liquid to solid ratio of 8:1 mL/g. The leaching mechanism was discussed via XRD, XPS, and FTIR. An efficient and green process for the recovery of valuable components in IPR has been developed. This research achieves the sufficient extraction of valuable components in IPR and provides significant guidance for the management of similar solid waste.