Structural Study of Diketopyrrolopyrrole Derivative Thin Films: Influence of Deposition Method, Substrate Surface,...

We report the morphology and microstructure of n-dialkyl side-chain-substituted thiophene DPP end-capped with phenyl groups (Ph-TDPP-Ph) thin films and compare the influence of deposition method and substrate surface using thermally oxidized Si and graphene substrates as well as monolayer graphene surfaces with an underlying self-assembled octadecyltrichlorosilane monolayer, complemented by an aging study of spin-coated films over a 2 weeks aging period. A distinct difference in morphology was observed between spin-coated and vacuum-deposited thin films, which formed a fiber-like morphology and a continuous layer of terraced grains, respectively. After an initial film evolution, all combinations of deposition method and substrate type result in well-ordered thin films with almost identical crystalline phases with slight variations in crystallinity and mosaicity. These findings point toward strong intermolecular forces dominating during growth, and the templating effect observed for other oligomer films formed on graphene is consequently ineffective for this material type. Upon aging of spin-coated films, a noticeable evolution involving two different morphologies and crystalline phases were observed. After several days, the thin film evolved into a more stable crystal phase and a fiber-like morphology. Moreover, slight variation in optical spectra were elucidated on the basis on density functional theory calculations. These results demonstrate that thin-film properties of DPP derivatives can be tailored by manipulating the film formation process.