Preparation of degradable chemically cross-linked polylactic acid films and its application on disposable straws

The semi-rigidity of the polylactic acid (PLA) molecular chain makes it brittle, poor impact resistance and barrier properties, which severely limits its practical applications. In this paper, a bio-based reactive plasticizer epoxy soybean oil (ESO) was used to improve the mechanical and barrier properties of maleic anhydride grafted polylactic acid (MAPLA) by the chemical reaction between the epoxy and anhydride group. Firstly, the optimum curing conditions were 93.5 °C, 100 °C, and 110.8 °C for 2 h. The effects of different mass fractions of ESO on the properties of MAPLA-ESO (ME) films were systematically investigated. It was found that when the content of ESO was 10 wt%, the tensile properties of the resulting ME films were the best, with a tensile strength of 35.2 MPa. And it had an elongation at break of 20.0 % and toughness of 5.4 MJ/m³, which increased to 690 % and 675 %, respectively, compared with pure MAPLA films. The chemically crosslinked ME films also displayed excellent water resistance, well degradation, low migration properties, and better performance than that of commercial paper straws and PLA straws, exhibiting great application potential as degradable disposable straws. Therefore, this work provides an effective way to develop high-performance, green, and degradable PLA films and products.