Mechanism Study of the Polymerization of Polyamide 56: Reaction Kinetics and Process Parameters

Polyamide 56 (PA56) has gained significant attention in the academic field due to its remarkable mechanical and thermal properties as a highly efficient and versatile biobased material. Its superior moisture absorption property also makes it a unique advantage in the realm of fiber textiles. However, despite extensive investigations on PA56's molecular and aggregate state structure, as well as processing modifications, little attention has been paid to its polymerization mechanism. Herein, the influence of temperature and time on PA56's polycondensation reaction is detailed studied by end-group titration and carbon nuclear magnetic resonance (NMR) techniques. The reaction kinetics equations for the pre-polymerization and vacuum melt-polymerization stages of PA56 are established, and possible side reactions during the polycondensation process are analyzed. By optimizing the reaction process based on kinetic characteristics, PA56 resin with superior comprehensive properties (melting temperature of 252.6 °C, degradation temperature of 371.6 °C, and tensile strength of 75 MPa) is obtained. The findings provide theoretical support for the industrial production of high-quality biobased PA56.