Synthesis and Characterization of Photo-Cross-Linkable Silk Fibroin Methacryloyl Hydrogel for Biomedical Applications

Photo-cross-linkable hydrogels have recently gained increased interest in the field of biomedical applications. In this study, silk fibroin was derivatized with methacrylic anhydride (MA) to obtain silk fibroin methacryloyl (SFMA), forming hydrogel under UV light exposure in 1 min. The SFMA sol-gel transition did not involve significant structural change at the early stage. Then, the formation of the irreversible β-sheet was confirmed after 24 h. The resulting SFMA hydrogel showed a homogeneous porous structure with pore sizes ranging from 400 to 700 μm, depending on the content. In addition, these hydrogels demonstrated a lower swelling capacity, higher rheological properties and compressive modulus, and slow degradation behavior at higher content, likely due to the higher degree of cross-linking. An experiment with cells indicated the good cell compatibility of these hydrogels, as revealed by Cell Counting Kit-8 (CCK-8) assays. As a tissue-engineered material, this photo-cross-linkable SFMA is expected to have a wide range of applications in the biomedical field.