A Three-Dimensional (3D) Framework of Freestanding Vanadium Nitride Nanowires for Dendrite-Free and Long Life-Span
Xiaoyu Feng1, Xian Huang1, Biao Gao1
1The State Key Laboratory of Refractories and, Metallurgy and Institute of Advanced Materials and Nanotechnology, Wuhan University of Science and Technology, 430081, Wuhan, China.
Abstract:
Lithium (Li) metal is a promising anode candidate for high-energy-density batteries owing to its high theoretical capacity and low electrochemical potential. However, uneven Li nucleation, uncontrollable dendritic growth, infinite voltage change and even safety issues hinder its commercial application. Herein, a three-dimensional (3D) framework of freestanding vanadium nitride nanowires (VN NWs) is established as Li host for dendrite-free Li metal anode. A lithiophilic Li3 N interlayer which in situ formed by the surface reaction between molten Li and VN NWs is utilized to guide a uniform Li nucleation and deposition within the skeleton, as well as avoid the dendrite formation. Meanwhile, VN NWs can decrease local current density, homogenize Li-ion flux and accommodate volume fluctuations of the anode due to its 3D structure with high electron conductivity. Thus, the corresponding composite Li metal anode delivers a long-life span of 500 cycles (1000 h) at a current density of 0.5 mA cm-2 , and exhibits lower nucleation over-potential and voltage hysteresis at different current densities from 0.5~5 mA cm-2 in carbonate electrolyte. In conclusion, this work provides a new type of scaffold with both high electronic conductivity and excellent lithiophilicity for stable Li anodes.