On the Efficiency of Laser Alloying of Grey Cast Iron with Tungsten and Silicon Carbides

Cast iron is widely used in engineering production and in the surface alloying of workpieces, which is exploited to improve the properties of the material. Research on cast iron is still valid and needed for the manufacturing processes throughout the product life cycle. In this study, the gray, cast iron GJL 200 laser processing is described based on surface alloying with WC and SiC particulates. SEM analysis and XRD analysis, as well as microhardness testing and tribological behavior studies, were employed. It was revealed that laser alloying with carbide particulates affects structural, mechanical, and operational properties compared to cast iron in its initial state. Most importantly, the right choice of laser processing conditions can increase the wear resistance of the cast iron base. The wear resistance after WC alloying was 4-24 times higher compared to the initial material, while after SiC alloying, it was 2-18 times lower than that of the initial material.