Biocompatibility and antibacterial activity of MgO/Ca3(PO4)2 composite ceramic scaffold based on vat...

Recent advancements in medical technology and increased interdisciplinary research have facilitated the development of the field of medical engineering. Specifically, in bone repair, researchers and potential users have placed greater demands on orthopedic implants regarding their biocompatibility, degradation rates, antibacterial properties, and other aspects. In response, our team developed composite ceramic samples using degradable materials calcium phosphate and magnesium oxide through the vat photopolymerization (VP) technique. The calcium phosphate content in each sample was, respectively, 80 %, 60 %, 40 %, and 20 %. To explore the relationship between the biocompatibility, antibacterial activity, and MgO content of the samples, we cultured them with osteoblasts (MC3T3-E1), Escherichia coli (a gram-negative bacterium), and Staphylococcus aureus (a gram-positive bacterium). Our results demonstrate that as the MgO content of the sample increases, its biocompatibility improves but its antibacterial activity decreases. Regarding the composite material samples, the 20 % calcium phosphate content group exhibited the best biocompatibility. However, after 0.5 h of co-cultivation, the antibacterial rates of all groups except the 20 % calcium phosphate content group co-cultured with S. aureus exceed 80 %. Furthermore, after 3 h, the antibacterial rates against E. coli exceed 95 % in all groups. This is because higher levels of MgO correspond to lower pH values and Mg²⁺ concentrations in the cell and bacterial culture solutions, which ultimately promote cell and bacterial proliferation. This elevates the biocompatibility of the samples, albeit at the expense of their antimicrobial efficacy. Thus, modulating the MgO content in the composite ceramic samples provides a strategy to develop gradient composite scaffolds for better control of their biocompatibility and antibacterial performance during different stages of bone regeneration.