Longevity of extrinsic stains on monolithic zirconia restorations: An in vitro study

Three-mol% yttria-stabilized tetragonal zirconia polycrystal (3Y-TZP) has been commonly used for fixed prosthodontic restorations. The opacity of 3Y-TZP may be masked with external staining, although the longevity of extrinsic stains applied to monolithic zirconia is unclear.

The purpose of this in vitro study was to analyze the color and surface roughness of extrinsically stained zirconia specimens after thermocycling and toothbrushing.

Monolithic Ø12.5×1.25-mm zirconia disks were milled from 3Y-TZP blocks, sintered according to manufacturer instructions, and then divided into 3 groups (C, J, and O; n=16) for application of stain and glaze. All specimens underwent 10 000 thermocycles in distilled water before being further divided into 2 dentifrice groups (n=8): normal grit, low relative dentin abrasivity (RDA) (Subgroup N) and abrasive grit, high RDA (Subgroup A). Specimens were brushed in a multistation brushing machine under 1.47 N of force using a 5:8 toothpaste and distilled water slurry for 10 000 cycles with a straight (American Dental Association Standard) toothbrush to simulate 1 year of toothbrushing. Color and surface roughness measurements were obtained at 3 time points: baseline, after thermocycling, and after brushing. A 2-way repeated measures ANOVA was used to independently assess changes in color and surface roughness with respect to thermocycling and brushing (α=.05).

Group J displayed no significant change in color for either dentifrice system (P>.05). However, a significant change in surface roughness was observed for both dentifrice subgroups (P<.001). Group C specimens displayed significant changes in color (P<.001) and surface roughness (P<.001) for both dentifrice systems. Group O specimens displayed significant changes in color (P<.025) for both dentifrice systems and significant changes in surface roughness (P<.004) for subgroup A, but no significant changes for subgroup N (P=.075).

Artificial aging of monolithic zirconia resulted in changes in color and surface roughness that did not surpass the thresholds for perceptibility and acceptability. This study failed to establish durability limits for extrinsic stains applied to 3Y-TZP.