The Improved Microwave Absorption Performance of the 3D Porous (Ni@NO-C)_n/NO-C Composite Absorber

Microwave absorbers that are lightweight and have good stability and high efficiency have attracted much attention for their applications in many contemporary fields. In this work, a 3D porous (Ni@NO-C)_n/NO-C composite absorber was prepared using a wet chemistry method with Ni chains and melamine as precursors, in which NO-C (N,O-doped carbon)-encapsulated Ni particles are homogenously dispersed in the 3D porous networks of NO-C in the form of (Ni@NO-C)_n chains. The special microstructure of the as-prepared material is proven to be beneficial for the improvement of its microwave absorption performance. The as-synthesized (Ni@NO-C)_n/NO-C composite absorber exhibited an effective absorption bandwidth of 4.1 GHz and an extremely large reflection loss of -72.3 dB. The excellent microwave-absorbing performances can be ascribed to the cooperative consequences of dielectric loss and magnetic loss, along with the balance between attenuation capability and impedance matching.