Adsorption and Dispersion Effect of Sodium Lignosulfonate on Fine SiC Particles in Aqueous Media

This study presented a novel modification method for fine SiC powder by using sodium lignosulfonate as a dispersant. The adsorption behavior of sodium lignosulfonate on the SiC/water interface and its effect on the performance of a fine SiC slurry were systematically investigated. The adsorption results showed that sodium lignosulfonate formed monolayer adsorption on the surface of fine SiC and that the saturated adsorption capacity was 1.3263 mg/g. The adsorption reached equilibrium within 3 h and was mainly controlled by active sites on the SiC surface. The dispersion, stability, and zeta potential of modified SiC powder were improved after sodium lignosulfonate adsorption. The zeta potential of modified SiC reached a minimum value of -44.8 mV at pH 12. Modified SiC suspensions had great stability in a wider pH range of 6-12. Modified SiC slurry with 54 vol % solid loading had a low viscosity of 173 mPa·s at pH 10. Subsequently, coarse SiC powder was added for slip casting. A mixed slurry with high solid loading (69 vol %) and low viscosity (583 mPa·s) was prepared using modified SiC and coarse SiC powders at a mass ratio of 2:3. Finally, recrystallized SiC green body with high density (2.6492 g/cm³) was obtained.