In solution-processed organic light-emitting diodes (OLEDs), achieving high color purity and efficiency is as important as that in vacuum processes. Emitters suitable for solution processing must have excellent solubility in organic solvents, high molecular weight, and compatibility with the host materials. In this study, we synthesized a deep-blue emitter that satisfies the above conditions by introducing a 1,4-bis(indolo[3,2,1-jk]carbazol-2-yl)benzene-based planar emitting core (DICz) structure and four 3,6-di-tert-butyl-9-phenyl-9H-carbazole (tCz) peripheral units, namely, 4tCz-DICz. A comparative compound, 4Hex-DICz, incorporating hexyl phenyl groups was synthesized. In contrast to 4Hex-DICz, 4tCz-DICz exhibited exceptional solubility in organic solvents and superior film-forming properties attributed to the presence of tCz units. Additionally, in the film state, the effective encapsulation of the emitting core (DICz) by the tCz units in 4tCz-DICz helps prevent undesirable molecular aggregation. The solution-processed OLEDs employing the CH-2D1 film, doped with 5 wt % 4tCz-DICz as the emitting layer, exhibited a deep-blue emission at 424 nm, characterized by a narrow bandwidth of 22 nm, and achieved a maximum external quantum efficiency (EQE) of approximately 4.0%. In contrast, the 4Hex-DICz-based device demonstrated an EQE of 2.91%. Consequently, we have successfully demonstrated that the introduction of four bulky tCz units into the DICz core is a promising molecular design strategy for the development of soluble indolocarbazole-based emitters, especially those used in high-performance deep-blue fluorescent OLEDs.