Hydrogel Membranes from Chitosan-Fish Gelatin-Glycerol for Biomedical Applications: Chondroitin Sulfate Incorporation...

Chondroitin sulfate (ChS), chitosan (Chi), and fish gelatin (FG), which are byproducts of a fish-treatment small enterprise, were incorporated with glycerol (Gly) to obtain dense hydrogel membranes with reduced brittleness, candidates for dressing in wound healing applications. The mechanical properties of all samples were studied via Dynamic Mechanical Analysis (DMA) and tensile tests while their internal structure was characterized using Attenuated Total Reflectance-Fourier Transform Infrared Spectroscopy (ATR-FTIR) and X-ray Diffraction (XRD) instruments. Their surface morphology was analyzed by ThermoGravimetric Analysis (TGA) method, while their water permeability was estimated via Water Vapor Transmission Rate (WVTR) measurements. Wettability and degradation rate measurements were also carried out. Characterization results indicated that secondary interactions between the natural polymers and the plasticizer create the hydrogel membranes. The samples were amorphous due to the high concentration of plasticizer and the amorphous nature of the natural polymers. The integration of ChS led to decreased decomposition temperature in comparison with the glycerol-free sample, and all the materials had dense structures. Finally, the in vitro endothelial cell attachment studies indicate that the hydrogel membranes successfully support the attachment and survival of primary on the hydrogel membranes and could be appropriate for external application in wound healing applications as dressings.