Toothbrushing effects on the surface roughness and cement volume loss of bonded enamel-ceramic interface

This study evaluated the effect of toothbrushing on enamel-cementing material-ceramic bonded interfaces, using different cementing materials.

Thirty enamel and thirty ceramic blocks were bonded with cementing materials to produce the samples that were bonded with three types of cementing materials: 1- RelyX Ultimate resin cement (REXU), 2- RelyX Unicem 2 self-adhesive resin cement (REU2) and 3- heated Z100 restorative composite (60°C). Bonded interfaces of the samples were toothbrushed and the surfaces of the 3 cementing materials were evaluated for roughness (RG, in µm), roughness profile (RP, in µm), and volume loss (VL, in µm3) (baseline and after 20,000 and 60,000 toothbrushing cycles). Data were evaluated by Generalized Linear Analysis (two factors: "material" and "toothbrushing cycle") and Bonferroni test (α=0.05).

REXU and Z100 exhibited lower RG than that presented by REU2, except after 60,000 toothbrushing cycles when only Z100 differed from REU2. The increase in toothbrushing cycles increased the RG and RP for all materials. REU2 also showed higher RP than those showed by REXU and Z100 when it was analyzed regarding the enamel. The VL of Z100 was the lowest with 20,000 toothbrushing cycles, regarding the enamel and ceramic. For 60,000 cycles, REXU showed the lowest VL regarding the ceramic, and REU2 had the highest VL regarding the enamel and ceramic.

In general, REXU and Z100 showed the best results regarding the evaluations performed and the REU2 exhibited the highest RG, RP, and VL.