Multiscale Modeling of a Chain Comprising Selective Laser Melting and Post-Machining toward Nanoscale Surface Finish

The generation of rough surfaces is an inherent drawback of selective laser melted (SLM) material that makes post-treatment operation a mandatory process to enhance its surface condition and service performance. However, planning an appropriate and optimized chain to attain the best surface finish needs an integrated simulation framework that includes physics of both additive manufacturing and post-processing. In the present work, an attempt is made to model the alternation of surface roughness which is produced by SLM and post-processed by milling and sequential surface burnishing. The framework includes a series of closed-form analytical solutions of all three processes embedded in a sequence where the output of the preceding operation is input of the sequential one. The results indicated that there is close agreement between the measured and predicted values of arithmetic surface roughness for both SLM material and the post-processed ones. It was also found that a nanoscale surface finish is obtained by finishing milling and single pass rolling at a static force of 1500 N. In addition, the results of the simulation showed that elimination of the milling process in the chain resulted in a six-times-longer production time that requires three times bigger rolling force compared to a chain with an included milling operation.