Role of Laser Powder Bed Fusion Process Factors in Determining the Porosity Formation in 3D Printing of Stainless...

In this study, an analytical model was developed to evaluate the influence of laser powder bed fusion (LPBF) process parameters on process-induced porosity during the 3D printing of stainless steel 316L. First, the temperature distribution, governed by a moving point heat source model of the laser, was used to predict the melt pool geometry during the melting stage. This prediction was then refined to account for the formation of the solidified cap. By analyzing the interaction between melt pool size and other process parameters, such as hatch spacing and layer thickness, criteria were established to distinguish between porosity caused by lack of fusion, porosity due to keyhole formation, and defect-free samples. A series of experiments were conducted, and porosity was measured using micro-CT analysis. The results showed that the porosity predicted by the model remained within an acceptable error range compared with the experimental measurements, with errors ranging from 10.5% to 24.78% and a mean error of 16.48%, demonstrating the accuracy of the developed model.