A Simple Synthesis and Microstructure Analysis of Human Peptide LL-37@Gold Nanoparticles (Known as LL-37@AuNPs)...

The basis of the present study is a straightforward method involving fewer chemical species for conjugating gold nanoparticles (AuNPs) with the antimicrobial peptide LL-37 designated as LL-37@AuNPs. Investigating the microstructure characteristics of the resulting materials and their potential as antibacterial and wound-healing substances are the main objectives of this study. Zeta (ζ) potential, Fourier transform infrared (FTIR), X-ray diffraction (XRD), field effect scanning electron microscopy (FE-SEM), energy dispersive X-ray diffraction (EDS), transmission electron microscopy (TEM), and UV-Vis spectrophotometry were used to analyze the physico-chemical properties of LL-37@AuNPs. The magnitude of LL-37's zeta potential and the LL-37@AuNPs show that the specimens are electrically stable and resistant to flocculation and coagulation. The surface plasmon resonance (RPS) of AuNPs, which is positioned at a wavelength of about 531 nm, was found to be unaffected by the presence of the LL-37 antimicrobial peptide. The FTIR data show the functional group characteristics of the LL-37@AuNPs vibration bands, and the XRD diffractogram confirms the formation of the LL-37@AuNPs conjugate nanocomposite. Based on FE-SEM and TEM data, the bulk of AuNPs were found to have a circular shape, with an average size of about 22.88 ± 8.21 nm. It was discovered that the LL-37@AuNPs had a good ability to inhibit S. aureus from growing. The wound-healing percentage reached 85% on day 12 of the trial, significantly greater than the results of the negative controls. LL-37@AuNPs(4) is the sample that had the highest percentage of wound healing between days 3 and 12. Moreover, sample LL-37@AuNPs(4) contains 0.45 µL of LL-37, whereas sample LL-37@AuNPs(2) contains 0.22 µL of LL-37. The faster wound-healing rate in LL-37@AuNPs(4) was believed to be due to a higher concentration of LL-37, which was able to stop S. aureus from developing while suppressing the inflammation surrounding the wound. The study's findings reveal that LL-37@AuNPs might be made using a straightforward process, making them a powerful antibacterial and therapeutic substance. However, before this discovery is applied in the field of medicine, a more thorough investigation is necessary.