Effect of Polyphenols on the Ultrastructure of the Dentin Pellicle and Subsequent Erosion

Erosive tooth wear is a highly prevalent dental condition that is modified by the ever-present salivary pellicle. The aim of the present in situ study was to investigate the effect of polyphenols on the ultrastructure of the pellicle formed on dentin in situ and a subsequent erosive challenge.

The pellicle was formed on bovine dentin specimens for 3 min or 2 h in 3 subjects. After subjects rinsed with sterile water (negative control), 1% tannic acid, 1% hop extract, or tin/fluoride solution containing 800 ppm tin and 500 ppm fluoride (positive control), specimens were removed from the oral cavity. The erosive challenge was performed on half of the specimens with 1% citric acid, and all specimens were analyzed by transmission electron microscopy. Incorporation of tannic acid in the pellicle was investigated by fluorescence spectroscopy.

Compared to the negative control, ultrastructural analyses reveal a thicker and electron-denser pellicle after application of polyphenols, in which, according to spectroscopy, tannic acid is also incorporated. Application of citric acid resulted in demineralization of dentin, but to a lesser degree when the pellicle was pretreated with a tin/fluoride solution. The pellicle was more acid-resistant than the negative control when modified with polyphenols or tin/fluoride solution.

Polyphenols can have a substantial impact on the ultrastructure and acid resistance of the dentin pellicle, while the tin/fluoride solution showed explicit protection against erosive demineralization.