Influence of Dilution on the Mechanical Properties and Microstructure of Polyurethane-Cement Based Composite Surface...

Polyurethane-cement composite are widely used in modern civil engineering, and the method of adding diluent is often used to adjust the construction process to adapt to the engineering environment. Studies have shown that the addition of diluent impacts the performance of polyurethane-cement based composite surface coatings, but there have been few reports on the influence of diluent content on the mechanical properties and microstructure of the coatings. To address this, polyurethane coatings with different diluent contents were prepared, and positron annihilation lifetime spectroscopy was used to test the microstructure of the coatings. The tensile strength and elongation at rupture were tested using a universal material testing machine, and the fracture interface morphology of each coating was observed by scanning electron microscopy. Finally, the correlation between the microstructure parameters and the mechanical properties of the coating was analyzed using grey relation theory. The results demonstrated that with the increase in diluent content, (i) the average radius of the free volume hole (R) and the free volume fraction (F) of the coating both showed a trend of first decreasing and then increasing. The value of R was between 3.04 and 3.24 Å, and the value of F was between 2.08 and 2.84%. (ii) The tensile strength of the coating increased first and then decreased, while the elongation at rupture decreased first and then increased. Among them, the value of tensile strength was between 3.23 and 4.02 MPa, and the value of elongation at fracture was between 49.34 and 63.04%. In addition, the free volume in polymers plays a crucial role in facilitating the migration of molecular chain segments and is closely related to the macroscopic mechanical properties of polymers. A correlation analysis showed that the R value of the coating had the greatest influence on its tensile strength, while F showed a higher correlation with the elongation at rupture.