Mussel-Inspired Calcium Alginate/Polyacrylamide Dual Network Hydrogel: A Physical Barrier to Prevent Postoperative
Zekun Su1, Beibei Xue1, Chang Xu2
1School of Materials Science and Engineering, Dalian University of Technology, Dalian 116024, China.
Abstract:
Intrauterine adhesions (IUA) has become one of the main causes of female infertility. How to effectively prevent postoperative re-adhesion has become a clinical challenge. In this study, a mussel-inspired dual-network hydrogel was proposed for the postoperative anti-adhesion of IUA. First, a calcium alginate/polyacrylamide (CA-PAM) hydrogel was prepared via covalent and Ca2+ cross-linking. Benefiting from abundant phenolic hydroxyl groups, polydopamine (PDA) was introduced to further enhance the adhesion ability and biocompatibility. This CA-PAM hydrogel immersed in 10 mg/mL dopamine solution possessed remarkable mechanical strength (elastic modulus > 5 kPa) and super stretchability (with a breaking elongation of 720%). At the same time, it showed excellent adhesion (more than 6 kPa). Surprisingly, the coagulation index of the hydrogel was 27.27 ± 4.91, demonstrating attractive coagulation performance in vitro and the potential for rapid hemostasis after surgery.