Repair bond strength of a new self-adhesive composite resin to three different resin-matrix ceramic CAD-CAM materials

Hande Kemaloglu1, Ozge Cay1, Elif Ercan Devrimci1

  • 1Department of Restorative Dentistry, Faculty of Dentistry, Ege University.

Dental Materials Journal
|January 17, 2024
PubMed

Keywords:
CAD-CAMSelf-adhesive flowable composite resinsShear bond strengthSilaneUniversal bonddental composite bondingCAD-CAM ceramicsself-adhesive resinrestorative dentistry

More Related Videos

Shrinkage of Dental Composite in Simulated Cavity Measured with Digital Image Correlation08:45

Shrinkage of Dental Composite in Simulated Cavity Measured with Digital Image Correlation

Published on: July 21, 2014

13.5K
Impact of Fabrication Techniques and Polishing Procedures on Surface Roughness of Denture Base Resins03:02

Impact of Fabrication Techniques and Polishing Procedures on Surface Roughness of Denture Base Resins

Published on: January 17, 2025

333

Related Concept Videos

Bonding and Strength of Aggregate01:12

Bonding and Strength of Aggregate

The bond between aggregate particles and the cement matrix is significantly influenced by the shape and surface texture of the aggregates. High-strength concretes benefit from a rougher texture, which leads to stronger bonding due to greater adhesion. Angular aggregates with larger surface areas also enhance this bond. The bonding quality, however, is complex to assess as no universally accepted test exists. Good bonding is indicated when a crushed concrete specimen shows some aggregate...
181
Strength of Cement01:20

Strength of Cement

Strength tests for cement are not performed directly on neat cement paste due to difficulty in obtaining consistent, reliable specimens. Instead, cement is typically tested in the form of cement-sand mortar.
For compressive strength tests, ASTM C 109-05 standards prescribe a cement-sand mix ratio of 1:2.75 and a water/cement ratio of 0.485 for making 2-inch cubes. These cubes are mixed, cast, and cured in saturated lime water at 23°C until testing. Flexural strength testing, outlined in...
138
Mortar Properties01:17

Mortar Properties

Mortar properties encompass a range of characteristics crucial for construction and masonry work, including workability, water retention, bond strength, durability, compressive strength, volume change, and appearance. Workability refers to mortar's ability to be easily applied and manipulated without sagging or falling off surfaces, which is important for efficient masonry unit placement and alignment. Water retention is essential to prevent the mortar from losing moisture too quickly to...
124
Composite Masonry Walls01:18

Composite Masonry Walls

Composite masonry walls combine multiple wythes of the same or different masonry materials to create a unified structure. These walls feature wythes that are bonded together either through mortar-filled collar joints, grouted spaces, or more commonly, with rigid metal ties and reinforcements, with the use of masonry header units being rare. Metal ties are preferred because they effectively minimize water penetration, as these walls primarily absorb moisture and then release it into the...
1.2K
Reinforcements in Concrete01:25

Reinforcements in Concrete

Reinforced concrete is a composite material used extensively in construction, combining the compressive strength of concrete with the tensile strength of steel. This synergy is essential as concrete, while excellent at resisting compression, is weak under tension. Steel bars, or rebars, are embedded in the concrete to handle these tensile forces. The choice of steel is strategic; it shares a similar coefficient of thermal expansion with concrete, which ensures uniformity in response to...
87