Effect of Vanadium Addition on Solidification Microstructure and Mechanical Properties of Al-4Ni Alloy

The effects of vanadium addition on the solidification microstructure and mechanical properties of Al-4Ni alloy were investigated via thermodynamic computation, thermal analysis, microstructural observations, and mechanical properties testing. The results show that the nucleation temperature of primary α-Al increased with increased vanadium addition. A transition from columnar to equiaxed growth took place when adding vanadium to Al-4Ni alloys, and the average grain size of primary α-Al was reduced from 1105 μm to 252 μm. When the vanadium addition was 0.2 wt%, the eutectic nucleation temperature increased from 636.2 °C for the Al-4Ni alloy to 640.5 °C, and the eutectic solidification time decreased from 310 s to 282 s. The average diameter of the eutectic Al₃Ni phases in the Al-4Ni-0.2V alloy reduced to 0.14 μm from 0.26 μm for the Al-4Ni alloy. As the vanadium additions exceeded 0.2 wt%, the eutectic nucleation temperature had no obvious change and the eutectic solidification time increased. The eutectic Al₃Ni phases began to coarsen, and the number of lamellar eutectic boundaries increased. The mechanical properties of Al-4Ni alloys gradually increased with vanadium addition (0-0.4 wt%). The Al-4Ni-0.4V alloy obtained the maximum tensile strength and elongation values, which were 136.4 MPa and 23.5%, respectively. As the vanadium addition exceeded 0.4 wt%, the strength and elongation decreased, while the hardness continued to increase. Fracture in the Al-4Ni-0.4V alloy exhibited ductile fracture, while fracture in the Al-4Ni-0.6V alloy was composed of dimples, tear edges, and cleavage planes, demonstrating mixed ductile-brittle fracture. The cleavage planes were caused by the primary Al₁₀V and coarse Al₃Ni phases at the boundary of eutectic cells.