Related Experiment Video

Updated: Jul 5, 2025

Determination of the Friction Coefficients of Icy Pavements Under Different Amounts of Snowfall
12:21

Determination of the Friction Coefficients of Icy Pavements Under Different Amounts of Snowfall

Published on: January 6, 2023

3.0K

A quantitative methodology for measuring the social sustainability of pavement deterioration

Egemen Okte1, Jessica Boakye2, Mark Behrend3

  • 1Civil and Environmental Engineering, University of Massachusetts Amherst, 130 Natural Resources Rd, Amherst, MA, 01003, USA. eokte@umass.edu.

Scientific Reports
|January 24, 2024
PubMed

More Related Videos

Applicability Analysis of Assessment Methods for Morphological Parameters of Corroded Steel Bars10:24

Applicability Analysis of Assessment Methods for Morphological Parameters of Corroded Steel Bars

Published on: November 1, 2018

6.7K
Evaluating the Effect of Roadside Parking on a Dual-Direction Urban Street14:55

Evaluating the Effect of Roadside Parking on a Dual-Direction Urban Street

Published on: January 20, 2023

3.3K

Related Concept Videos

Abrasion Resistance of Concrete01:23

Abrasion Resistance of Concrete

Abrasion resistance is an essential characteristic of concrete that determines its durability and longevity under various wear conditions. Concrete surfaces are vulnerable to different types of abrasion. For instance, surfaces may wear down due to the constant movement of vehicles or be eroded by solids carried in water, as seen in concrete canal linings. Specific tests are conducted to measure the abrasion resistance of concrete.
One such test is the revolving disc test, where three plates...
133
Toughness and Hardness of Aggregate01:22

Toughness and Hardness of Aggregate

Toughness and hardness are critical properties of aggregate materials used in concrete, particularly on pavement surfaces and industrial flooring subjected to heavy loads. Toughness is defined as the aggregate's resistance to failure by impact and is measured by the aggregate impact value (AIV). For this, the aggregate impact value test is performed, wherein the impact is delivered by a standard hammer, which falls freely under its own weight onto the aggregates. The aggregates fragment in...
258
Design Example: Joints in Concrete Pavements01:28

Design Example: Joints in Concrete Pavements

Concrete pavement joints are essential for maintaining the structural integrity and longevity of pavement by controlling where and how the pavement cracks. These joints can be categorized based on their functions, such as contraction or control joints, construction joints, isolation joints, and expansion joints.
Contraction joints are typically formed by sawing a groove into the concrete shortly after it has hardened. This creates a weakened vertical plane, deliberately encouraging cracking at...
183
Microcracking in Concrete01:20

Microcracking in Concrete

Microcracking in concrete refers to the tiny cracks that can form within the material even before any external load is applied. These microcracks typically occur at the interface between the coarse aggregate and the hydrated cement paste, often as a result of differential volume changes prompted by variations in stress-strain behavior, as well as thermal and moisture movement. Initially, these microcracks remain stable and do not grow substantially until the concrete is stressed to about 30...
118
Unsoundness of Aggregate due to Volume Change01:26

Unsoundness of Aggregate due to Volume Change

Unsoundness in aggregates due to volume changes is primarily caused by the physical alterations aggregates undergo, such as freezing and thawing, thermal changes, and wetting and drying. Unsound aggregates, when subjected to these changes, result in volume change upon disintegration. This, in turn, contributes to the deterioration of concrete, including scaling, pop-outs, and cracking. Particular types of aggregates, such as porous flints, cherts, and those containing clay minerals, are...
113
Non-destructive Tests for Concrete Strength01:12

Non-destructive Tests for Concrete Strength

The rebound hammer test, also known as the Schmidt hammer test, is a non-destructive technique for evaluating the hardness of concrete and, indirectly, the strength of concrete. It operates on the principle that the rebound of a spring-driven mass from a concrete surface correlates to the surface's hardness. The device comprises a mass within a tubular housing, a spring mechanism, and a plunger that strikes the concrete. Upon release, the energy imparted to the mass by the spring causes it...
119