Comparison of Adhesion Performance of a Self-curing and a Light-curing Universal Adhesive to Various Dental...

To compare the adhesion of a self-curing (Tokuyama Universal Bond, TUB) and a light-curing (Scotchbond Universal, SBU) universal adhesive to CAD/CAM materials, enamel, and dentin. This study also assessed differences in enamel adhesion between self-etch vs selective etching modes, as well as immediate and long-term adhesion to dentin for both adhesives.

Shear bond strength (SBS) testing was used to assess adhesion to enamel, dentin, Lava Ultimate (LU), Vita Enamic (VE), IPS e.max CAD (LD), IPS e.max ZirCAD (3Y-Zir), and Lava Esthetic (5Y-Zir) (n = 10). Moreover, bonding to enamel in self-etch and selective etching modes (n = 10) as well as immediate and aged resin-dentin bond strength (24 h after bonding, after 100,000 thermal cycles [TC] and long-term storage) was evaluated using the microtensile bond-strength test (n = 30). Failure mode was also determined for the bonding to dentin. Statistical analyses consisted of one-way and two-way ANOVA with appropriate post-hoc Tukey-Kramer or two-sample t-tests, as well as the chi-squared or Fisher's exact test (α = 0.05).

TUB and SBU universal adhesives presented similar bonding to LU, VE, 3Y-Zir, and 5Y-Zir. However, SBS for TUB was superior to SBU when bonding to lithium-disilicate glass-ceramic (IPS e.max CAD). SBU showed better adhesion to dentin and enamel when used in the self-etch mode, while TUB promoted strong bond strength to enamel in the selective etching mode. TUB after TC was the only aging condition that yielded a significant reduction in resin-dentin bond strength.

In-vitro adhesion performance of the self-curing and light-curing universal adhesives varies depending on the dental substrate or CAD/CAM restorative material used for bonding.