A molecularly engineered fully bio-derived phosphorylated furan-based flame retardant for biomass-based fabrics

With the increasing awareness of environmental protection, the demand for eco-friendly bio-derived flame-retardant for textiles has received increasing attention. In this work, a fully bio-derived phosphorylated furan-based flame retardant (FAP) was synthesized by the Schiff reaction of furan-based compounds (furfural and furfurylamine). To evaluate the application scope and flame retardant efficiency of FAP, cotton fabrics and PLA nonwovens were selected as biomass-based representatives of natural fiber materials and synthetic fiber materials, respectively. Significantly, based on the composition of furan ring, phosphorus and nitrogen containing components of FAP, excellent charring and flame retardant properties of coated cotton fabrics and PLA nonwovens can be expected. TGA results showed that the residual char of C-FAP-3 and P-FAP-3 were 39.7% (increased by 267.6%) and 16.7% (increased by 215.1%), respectively, higher than those of control cotton (10.8%) and PLA nonwoven (5.3%). Cone test results exhibited that the peak heat release rate (PHRR) and total heat release (THR) values of C-FAP-3 were sharply decreased by 69.4% and 37.8%, respectively. P-FAP-3 also displayed a significant reduction in PHRR, implying high flame retardancy of C-FAP-3 and P-FAP-3. Notably, through the weight gains of FAP coating on cotton and PLA as well as the final LOI and VBT results of the flame retardant treated fabrics, it can be preliminarily inferred that control cotton fabrics are more likely to achieve better flame retardant effects than PLA. Additionally, the facile synthetic strategy of fully bio-derived flame retardants is expected to promote the development of green flame retardant strategies for high-performance textiles.