Characterization of a Novel TiF4 Inclusion Complex and in vitro Evaluation of Its Effect on Inhibiting Enamel
Elham Farhadi1, Ladan Ranjbar Omrani2, Khosrou Abdi3,4
1Department of Restorative Dentistry, School of Dentistry, Arak University of Medical Sciences, Arak, Iran.
Introduction:
Titanium tetrafluoride (TiF4) is an anticariogenic agent with high remineralizing potential. However, the acidic pH of TiF4 solution can limit its clinical application. The present study aimed to prepare and characterize a new TiF4-dendrimer inclusion complex and evaluate its ability to inhibit enamel demineralization under pH cycling conditions.
Methods:
PEG-citrate dendrimer and TiF4-dendrimer inclusion complex were synthesized and their molecular structures were evaluated using Fourier-transform Infrared Spectroscopy (FTIR), Hydrogen Nuclear Magnetic Resonance (HNMR), and Liquid Chromatography-Mass Spectrometry (LC-MS) tests. Forty-eight enamel samples were prepared and randomly divided into four groups: distilled water (negative control), TiF4 solution (T), dendrimer solution (D), and TiF4-dendrimer solution (TD). The microhardness of the samples was measured initially. Next, the samples underwent pH cycling, were exposed to the solutions, the microhardness was measured again, and microhardness loss was calculated. EDX analysis was performed on the surface and cross-sectional segments of the samples.
Results:
The microhardness loss was significantly higher in control (-65.1 ± 6.0) compared to other groups. No significant difference was observed between T (-47.9 ± 5.6) and D (-41.7 ± 12.0) and also D and TD (-40.5 ± 9.4) in this regard. Microhardness loss was significantly higher in T compared to TD group. The TD samples showed similar fluoride and titanium content in both surface and subsurface regions, while the T group had higher concentrations in the surface region. Moreover, the TD solution had a higher pH of 3.4 compared to the T solution's pH of 1.1.
Conclusion:
No significant difference was observed between the efficacy of TiF4-dendrimer and TiF4 solution in inhibiting demineralization while TiF4-dendrimer solution had the added advantage of having a higher pH.
Related Concept Videos
01:26EDTA: Auxiliary Complexing Reagents
01:22EDTA: Chemistry and Properties
02:46Crystal Field Theory - Tetrahedral and Square Planar Complexes
Crystal field theory (CFT) is applicable to molecules in geometries other than octahedral. In octahedral complexes, the lobes of the dx2−y2 and dz2 orbitals point directly at the ligands. For tetrahedral complexes, the d orbitals remain in place, but with only four ligands located between the axes. None of the orbitals points directly at the tetrahedral ligands. However, the dx2−y2 and dz2 orbitals (along the Cartesian axes) overlap with the ligands less than the dxy,...
01:19Masking and Demasking Agents
There are many masking agents, such as cyanide, fluoride, triethanolamine, thiourea, and 2,3-bis(sulfanyl)propan-1-ol (formerly 2,3-dimercapto-1-propanol), with the masking agent chosen based on...
02:58Crystal Field Theory - Octahedral Complexes
To explain the observed behavior of transition metal complexes (such as colors), a model involving electrostatic interactions between the electrons from the ligands and the electrons in the unhybridized d orbitals of the central metal atom has been developed. This electrostatic model is crystal field theory (CFT). It helps to understand, interpret, and predict the colors, magnetic behavior, and some structures of coordination compounds of transition metals.
CFT focuses on...
01:19Complexation Equilibria: The Chelate Effect