Comparison of the stress distribution in base materials and thicknesses in composite resin restorations

Resin-based composite materials are commonly used for restorations, but their dimensional changes during the polymerization could cause various clinical problems. This study evaluated the influence of a base of different materials and thicknesses on the stress magnitude and distribution in a second maxillary premolar with an MOD resin composite restoration using three-dimensional finite element analysis. A sound tooth without cavity was considered as the control group (ST), and another group was restored with composite resin without applying a base material in a MOD cavity (CR). The other three groups were restored with composite resin along with the following base materials: glass ionomer cement, low-viscosity resin, and tricalcium silicate, respectively (CR-GIC, CR-LR, and CR-TS). These three groups were further divided into two subgroups according to the thickness of the base layer: thin (0.5 mm) and thick (1.0 mm). The stress distribution was compared using the maximum principal stress after polymerization shrinkage and vertical loading with 600 N on the occlusal surface. Group ST showed the lowest stress value, and its stress propagation was confined to outer enamel surfaces only. Group CR demonstrated the highest stress distribution in the tooth-restoration interface with increased failure risk on marginal areas. The thin and thick subgroups of the three groups with a base layer had lower stress levels than Group CR. The base materials reduced the marginal stress caused by polymerization shrinkage of composite resin in MOD cavities. Different base materials and thicknesses did not affect the stress distribution.