Efficient Single-Phase Tunable Dual-Color Luminescence with High Quantum Yield Greater than 100% for Information...

In modern society, the investigation of highly efficient photoluminescent bulk materials with excitation-induced tunable multicolor luminescence and multiexciton generation (MEG) is of great significance to information security and the application of optoelectronic devices. In this study, two bulk Cu-based halide crystals of (C₄H₁₀NO)₄Cu₂Br₅·Br and (C₄H₁₀NO)₄Cu₂I₅·I·H₂O, respectively, with one-dimensional structures were grown by a solvent evaporation method. Unexpectedly, (C₄H₁₀NO)₄Cu₂I₅·I·H₂O displayed excitation-induced tunable dual-color luminescence; one band is a brilliant green-yellow emission centered at 547 nm with a high photoluminescence quantum yield (PLQY) of up to 169.67%, and the other is a red emission at 695 nm with a PLQY of 75.76%. Just as importantly, (C₄H₁₀NO)₄Cu₂Br₅·Br exhibits a strong broadband green-yellow emission at 561 nm under broad band excitation ranging from 252 to 350 nm, a long PL decay lifetime of 106.9 μs, and an ultrahigh PLQY of 198.22%. These materials represent the first two examples of 1D bulk crystals and Cu(I)-based halides that have a PLQY exceeding 100%. Combining the unusual luminescence characteristics with theoretical calculations reveals that MEG contributes to the green-yellow emission with ultrahigh PLQY > 100%, and that the red emission can be ascribed to [Cu₂I₅]^3- cluster-centered emission. Additionally, an information encryption method was designed based on the Morse Code. The high luminescence characteristics of LED devices fabricated using the (C₄H₁₀NO)₄Cu₂Br₅·Br and (C₄H₁₀NO)₄Cu₂I₅·I·H₂O crystals appear to lead to promising applications in solid-state lighting. This work extends the catalog of high-performance luminescent materials and also promotes application prospects of low-dimensional copper-based halides in optoelectronics.