Corrosion-induced changes in surface properties and roughness of orthodontic wires

This study aimed to investigate the surface free energy and surface roughness (SR) of metallic alloys under the influence of acid solutions.

The experiment involved the use of 270 rectangular wire samples measuring 0.019 × 0.025-in. These samples were sourced from 3 different commercial brands: Dentsply GAC, American Orthodontics, and Orthoclassic. This in vitro study categorized the samples into 3 groups based on the solutions employed: deionized water, citric acid, and phosphoric acid. Each group consisted of 90 samples, with 30 samples representing each type of alloy-stainless steel, nickel-titanium, and titanium molybdenum alloy (TMA). The wire segments were immersed in their respective solutions for 72 hours at a controlled temperature of 37°C, with continuous orbital agitation at 130 rpm. After the immersion period, the study analyzed both surface free energy and SR. The mean values obtained were subjected to an analysis of variance at a significance level of 5%.

All alloys displayed hydrophobic behavior, as indicated by interaction free energy values <0. In acidic environments (phosphoric acid and citric acid), significant differences were observed among different brands and alloys, affecting surface energy and interaction free energy. Variations in SR among metallic alloys included steel with the lowest SR variations, followed by nickel-titanium and TMA. Notably, the TMA alloy stood out with significantly higher surface energy compared with that of the other alloys (P <0.001).

In this study, all examined alloys demonstrated a hydrophobic nature, suggesting a limited attraction to water. Notably, TMA exhibited the least hydrophobic behavior among the alloys studied. However, when exposed to citric acid, TMA displayed the most substantial alterations in its surface properties. These results underscored the significance of accounting for the distinctive properties of each alloy and their responses to diverse challenges, such as exposure to acidic solutions, during the selection of orthodontic wires for orthodontics treatment.