Evaluation of surface microhardness and gingival marginal adaptation of three different bulk-fill flowable resin
Nourhan Medhat Khairy1, Naglaa Rizk Elkholany1, Abeer Elsayed Elembaby1
1Conservative Dentistry Department, Faculty of Dentistry, Mansoura University, Mansoura, Aldakhlia, Egypt.
Objectives:
To evaluate surface microhardness and gingival marginal adaptation of three different bulk-fill flowable resin composites (FB-RBCs) in Class V cavities with enamel or dentin margins before and after thermocycling (TMC).
Materials And Methods:
Three available FB-RBCs were used; Palfique Bulk Flow (PaBF) (Tokuyama Dental), SDR Flow+ Bulk Fill Flowable (Dentsply Sirona), and I-Flow Bulk Fill (I-Dental). Thirty discs were prepared from each type of FB-RBCs. The discs were subjected to Vickers microhardness tester machine. Class V cavities were prepared on 180 molars. Gingival margins of half the specimens were prepared above CEJ and the other half below CEJ. Cavities were restored with FB-RBCs for gingival marginal adaptation test. Two-way ANOVA was used in microhardness, while three-way ANOVA was used for marginal adaptation.
Results:
The used materials showed statistically significant differences in microhardness and marginal adaptation.
Conclusions:
Regarding microhardness, PaBF showed the highest value before TMC and SDR was the highest after TMC. Regarding marginal adaptation, SDR revealed the best marginal adaptation than PaBF and I-flow, either subjected to TMC or not.
Clinical Significance:
The longevity of cervical restorations depend on both the location of the cavity margin and the material used. The microfractures in resin composite surface due to low surface microhardness as well as marginal gaps seen in laboratory studies could be considered as an indicative parameter for clinical problem associated with marginal differences.
More Related Videos
07:42Quasistatic Mechanical Testing for Computer-Aided Design and Manufacturing Occlusal Veneers Cemented to Milled Dentin Analog Material
Published on: December 20, 2024
06:16Author Spotlight: Establishing an Accurate Microhardness Testing Protocol for Craniofacial Tissues
Published on: April 26, 2024