Amino-Modified Graphene Oxide from Kish Graphite for Enhancing Corrosion Resistance of Waterborne Epoxy Coatings

Waterborne epoxy (WEP) coatings with enhanced corrosion resistance were prepared using graphene oxide (GO) that was obtained from kish graphite, and amino-functionalized graphene oxide (AGO) was modified by 2-aminomalonamide. The structural characteristics of the GO and AGO were analyzed using X-ray diffraction (XRD), Raman spectroscopy, Fourier transform infrared spectroscopy (FT-IR), scanning electron microscopy (SEM), and transmission electron microscopy (TEM). And the anti-corrosive performance of waterborne epoxy-cased composite coatings with different addition amounts of AGO was investigated using electrochemical measurements, pull-off adhesion tests, and salt spray tests. The results indicate that AGO15/WEP with 0.15 wt.% of AGO has the best anti-corrosive performance, and the lowest frequency impedance modulus increased from 1.03 × 10⁸ to 1.63 × 10¹⁰ ohm·cm^-2 compared to that of WEP. Furthermore, AGO15/WEP also demonstrates the minimal corrosion products or bubbles in the salt spray test for 200 h, affirming its exceptional long-term corrosion protection capability.