Seamless integration of a nickel-based metal-organic framework with three-dimensional substrates for nonenzymatic...

The effective integration of nanomaterials with underlying current collectors is a key factor affecting the performance of nonenzymatic glucose sensors, where an inappropriate integration structure often leads to poor electron transport and instability. In this work, a seamless integrated electrode was constructed by the in situ immobilizing of a nickel-based metal-organic framework (Ni-MOF) on a three-dimensional (3D) conductive nickel foam (NF) for highly sensitive and durable glucose sensing. Facilitated by a rapid microwave-assisted reaction, a robust interfacial interaction between the Ni-MOF and the substrate was established through in situ conversion from nickel oxide (NiO). The fabricated Ni-MOF/NF electrode exhibits an excellent limit of detection (LOD) of 2.65 μM and an impressive sensitivity (14.31 mA cm^-2 mM^-1) within the linear range (4-576 μM), which is significantly boosted compared with that of an electrode prepared by a typical drop-casting method (3.56 mA cm^-2 mM^-1 in 4-1836 μM). Characterization and electrochemical tests reveal that this integrated structure on the one hand contributes to fast electron transport and thus has enhanced sensitivity and on the other hand leads to exceptional durability with its structural integrity maintained under bending, shaking, and ultrasonication. Moreover, this seamless integration method was also employed to immobilize the Ni-MOF converted from the pre-chemically deposited NiO layer on another type of substrate, 3D carbon paper (CP), demonstrating the versatility of this facile strategy in creating diverse electrochemical electrodes for applications beyond glucose sensing.