Demonstration of 651 nm InGaN-based red light-emitting diode with an external quantum efficiency over 6% by InGaN/AlN...

This work reports a high-performance InGaN-based red-emitting LED with a strain-release interlayer (SRI) consisting of an InGaN stress-release layer (SRL) and an AlN dislocation confinement layer (DCL) in unintentionally doped GaN (u-GaN). The SRL introduces a tensile strain which could decrease the in-plane compressive stress of the u-GaN layer, while the DCL could reduce the dislocation density and thus improve the crystal quality of the u-GaN layer. Consequently, a high-efficiency InGaN-based red-emitting LED with a peak wavelength of 651 nm and an external quantum efficiency of 6.04% is realized. In addition, the room-temperature photoluminescence (PL) mapping emission wavelength is uniform across a 4-inch wafer with a standard deviation of 3.3 nm. Therefore, the proposed SRI offers good potential for mass-producing high-performance and long-wavelength InGaN-based red-emitting LEDs.