A biodegradable pH-response packaging film with blueberry extract: Blown-extrusion fabrication, multifunctional...

This work proposed a novel strategy for manufacturing biodegradable pH-response packaging. Briefly, to minimize the amount and thermal processing times of blueberry extract (BE), ethanol-dissolved BE (≤ 3‰ w/w) was sprayed onto the starch/poly(butylene adipate-co-terephthalate) (PBAT) pellets before extrusion blowing. BE was well-integrated into the matrix, forming uniformly colored films. The films with BE exhibited superior mechanical (7.85 MPa of strength, 606.53% of elongation) and enhanced barrier capabilities against ultraviolet light, moisture, and gas. Additionally, they exhibited good antioxidant capacity (68.69%), antibacterial activity (72.40%), and maintained color stability. The film with 3‰ w/w BE presented excellent color responsiveness (ΔE^⁎ ≥ 15) in the alkaline range, and successfully monitored the spoilage of shrimp. The pigments in the film had the maximum migration degree (≥ 70%) and rate in 50% ethanol simulation, following a first-order kinetic behavior dominated by Fickian diffusion. Findings supported the application of this strategy in the fabrication of starch/PBAT/BE films for pH-response intelligent packaging.