Antibacterial Efficacy of Mineral Trioxide Aggregate, Bioactive Glass and Epoxy-Resin Based Sealer: An In-Vitro...

The aim and objective of this in vitro study was to evaluate the antibacterial efficacy of mineral trioxide aggregate, bioactive glass sealer, and epoxy-resin-based sealer.

In the present study, 22 Mueller Hinton agar (MH agar) plates were employed and equally divided into two groups. Three holes were made by removal of agar at equidistant points and filled with root canal sealers. The strains of the bacteria used in this study were S. aureus (ATCC 6538) and C. albicans (ATCC 10231) and were divided into two groups and root canal sealers were divided into three subgroups: mineral trioxide aggregate (MTA) fillapex Sealer, Nishika Bioactive Glass sealer, and Syntex Epoxy Resin base sealer. For Staphylococcus aureus, peptone water was placed in a 2 mL test tube and bacteria were extracted from blood agar plates using a nichrome wire loop and poured into the peptone water-containing test tube and incubated for 2 hours and for C. albicans, fungi were grown at 37°C for 24 hours in MH Broth and seeded into MH agar to produce turbidity of 0.5 on the McFarland scale, which corresponds to a concentration of 10⁸ CFU/mL. This MH broth was used as a second layer. The seeded agar was then added over the plates immediately after the insertion of sealer cement. After incubation, the diameters of zones of inhibition around the plates were measured.

The results of this study showed that the highest inhibition was recorded in Syntex sealer against Staphylococcus aureus followed by MTA fillapex sealer and Nishika sealer, whereas MTA fillapex showed the highest inhibition against C. albicans followed by Syntex sealer and Nishika sealer.

Syntex sealer exhibits better antibacterial efficacy against Staphylococcus aureus and MTA fillapex exhibit better antibacterial efficacy against C. albicans.