Effect of radiation cross-linked collagen scaffold in alveolar ridge preservation of extraction socket

This study aimed to evaluate the properties of radiation cross-linked collagen scaffold (RCS) and its efficacy for alveolar ridge preservation (ARP). RCS was prepared from collagen dispersion by electron beam irradiation and freeze-drying. The microstructure, swelling ratio, area alteration and mechanical properties of RCS were characterized. Fifty-four New Zealand rabbits performing incisor extraction on maxilla and mandible were randomly assigned into positive, sham operation or treatment groups. Micro-computed tomography (micro-CT) scans, performed after 1, 4, and 12 weeks of surgery, were to assess changes in ridge height at buccal and palatal side, in ridge width and in micromorphological parameters. Histological analysis accessed socket microarchitecture. The results showed that RCS had stable mechanical properties and morphologic features that provided a reliable physical support for ARP. Dimensional changes in treatment group revealed significantly greater vertical height at buccal (5.32 [3.37, 7.26] mm, p < .0001) and palatal (4.37 [2.66, 6.09] mm, p < .0001) side, and horizontal width at the maxilla (0.16 [0.04, 0.28] mm, p < .01) and mandible (0.33 [0.11, 0.54] mm, p < .01) than those in sham operation group after 12 weeks. The treatment group had advantage than positive group in vertical height preservation, quantitatively. The order and density of bone trabeculae were improved in treatment group. These findings indicated that RCS had the potential to serve as an effective scaffold for ARP.