Evaluation and Modeling of Polylactide Photodegradation under Ultraviolet Irradiation: Bio-Based Polyester Photolysis...

In our study, we investigated the accelerated aging process of PLA under 253.7 nm UV-C irradiation with the use of the GPC, NMR, FTIR, and DSC methods and formal kinetic analysis. The results of GPC and DSC indicated a significant degree of destructive changes in the PLA macromolecules, while spectroscopic methods NMR and FTIR showed maintenance of the PLA main structural elements even after a long time of UV exposure. In addition to that, the GPC method displayed the formation of a high molecular weight fraction starting from 24 h of irradiation, and an increase in its content after 144 h of irradiation. It has been shown for the first time that a distinctive feature of prolonged UV exposure is the occurrence of intra- and intermolecular radical recombination reactions, leading to the formation of a high molecular weight fraction of PLA decomposition products. This causes the observed slowdown of the photolysis process. It was concluded that photolysis of PLA is a complex physicochemical process, the mechanism of which depends on morphological changes in the solid phase of the polymer under UV radiation.