Experimental investigation of ultrasonic assisted coating on three-point bending behavior of 3D printed polymeric...

3D printed Poly Lactic Acid (PLA) bone plates exhibit limited three-point bending strength, restricting their viability in biomedical applications. The application of polydopamine (PDM) enhances the three-point bending strength by undergoing covalent interactions with PLA molecular structure. However, the heavy nature of PDM particles leads to settling at the container base at higher coating solution concentrations. This study investigates the impact of ultrasonic-assisted coating parameters on the three-point bending strength. Utilizing Response Surface Methodology (RSM) for statistical modeling, the study examines the influence of ultrasonic vibration power (UP), coating solution concentration (CC), and submersion time (TIME). RSM optimization recommended 100 % UP, 6 mg/ml CC, and 150 min TIME, resulting in maximum three-point bending strength of 83.295 MPa. Microscopic images from the comparative analysis revealed non-uniform coating deposition with mean thickness of 6.153 µm under normal coating. In contrast, ultrasonic-assisted coating promoted uniform deposition with mean thickness of 18.05 µm. The results demonstrate that ultrasonic-assisted coating induces PDM particle collision, preventing settling at the container base, and enhances three-point bending strength by 7.27 % to 23.24 % compared to the normal coating condition. This study emphasizes on the potential of ultrasonic-assisted coating to overcome the limitations of direct immersion coating technique.