Synthesis and characterization of pH-sensitive nanocarrier based chitosan-g-poly(itaconic acid) for ciprofloxacin delivery for anti-bacterial application

This study aims to develop pH-sensitive and controlled release of ciprofloxacin from ciprofloxacin-loaded grafted chitosan-coated zinc oxide nanoparticles (Cip@Gchit/Zn-NPs) for the treatment of bacterial infections in the human colon. For this aim, first, the chitosan-g-poly(itaconic acid) [Chit-g-poly (Itac)] was synthesized via grafting of itaconic acid onto chitosan in the presence of cerium ammonium nitrate (CAN) under an inert atmosphere using conventional methods, while zinc oxide nanoparticles (Zn-NPs) were prepared via sol-gel technique. Characterization of the synthesized Cip@Gchit/Zn-NPs was analyzed using XRD, FT-IR, SEM, TGA, and zeta potential analysis. The antibacterial efficacy of Cip@Gchit/Zn-NPs against three pathogenic bacteria, namely Pseudomonas aeruginosa, Escherichia coli, and Staphylococcus aureus, was superior to that of tetracycline reference drugs, as evidenced by larger inhibition zones. Cytotoxicity assessment of Cip@Gchit/Zn-NPs on the human chondrocyte cell line C28/I2 via MTT assay revealed 100 % cell viability at a concentration of 500 μg/mL. The loading efficiency of ciprofloxacin into Gchit/Zn-NPs was evaluated at various ratios, demonstrating lower loading efficiency; however, sustained release of ciprofloxacin from Cip@Gchit/Zn-NPs was excellent, with 98.13 % release observed at pH 7.2 over 10 h. Kinetic analysis of ciprofloxacin release followed the first-order kinetic models.