Fuel Characteristics and Phytotoxicity Assay of Biochar Derived from Rose Pruning Waste

The aim of this study was the characterization and evaluation of applicability as a soil amendment of biochar derived from rose pruning waste at different pyrolysis temperatures (200-500 °C) and process durations (20-60 min). The biochar properties were compared to the raw material. The biochars produced at 300 °C for 40 and 60 min demonstrated the best fuel properties. These variants showed high energy gain rates (77.6 ± 1.5% and 74.8 ± 1.5%, respectively), energy densification ratios (1.35 ± 0.00 and 1.37 ± 0.00, respectively), high heating values (24,720 ± 267 J × g^-1 and 25,113 ± 731 J × g^-1, respectively), and relative low ash contents (5.9 ± 0.5% and 7.1 ± 0.3%, respectively). Regarding fertilizer properties, such as pH value, ash content, heavy metal content, and pollutant elution, the biochars showed better qualities than the raw material. All tested biochar did not exceed the permissible values for heavy metals, including Cr, Cd, Ni, and Pb. The most optimal properties for soil amendments were noted for biochar variants of 400 °C for 40 min, 450 °C for 20 min, and 500 °C for 20 min. Generally, biochars produced at temperatures ≥400 °C did not inhibit root elongation, except for the material produced at 450 °C for 60 min (4.08 ± 23.34%). Biochars obtained at ≥300 °C showed a positive impact on seed germination (86.67 ± 18.48-100 ± 24.14%).