Magnetoelectric Properties of Multiferroic Composites Based on BaTiO₃ and Nickel-Zinc Ferrite Material

The purpose of the present study was to learn the morphological, structural, ferroelectric, dielectric, electromechanical, magnetoelectric, and magnetic properties, and DC conductivity of BaTiO₃-Ni_0.64Zn_0.36Fe₂O₄ (BT-F) multiferroic composites compacted via the free sintering method. The influence of the ferrite content in ceramic composite materials on the functional properties is investigated and discussed. X-ray diffraction studies confirmed the presence of two main phases of the composite, with strong reflections originating from BaTiO₃ and weak peaks originating from nickel-zinc ferrite. BT-F ceramic composites have been shown to exhibit multiferroism at room temperature. All studied compositions have high permittivity values and low dielectric loss, while the ferroelectric properties of the BT component are maintained at a high level. On the other hand, magnetic properties depend on the amount of the ferrite phase and are the strongest for the composition with 15 wt.% of F (magnetization at RT is 4.12 emu/g). The magnetoelectric coupling between BT and F phases confirmed by the lock-in technique is the largest for 15 wt.% ferrite. In the present work, the process conditions of the free sintering method for obtaining BT-F multiferroic composite with good electrical and magnetic properties (in one material) were optimized. An improved set of multifunctional properties allows the expansion of the possibilities of using multiferroic composites in microelectronics.