Mechanical Properties and Performance of 3D-Printed Acrylonitrile Butadiene Styrene Reinforced with Carbon, Glass and...

This paper presents the results of experimental investigation of the mechanical characteristics of 3D-printed acrylonitrile butadiene styrene (ABS) and its modifications reinforced with different types of short-fiber fillers: carbon, glass, and basalt. Elastic modulus, tensile and bending strength, as well as fracture toughness were determined in series of mechanical tests for samples produced with different manufacturing parameters, such as nozzle diameter and infill angle. It was found that the use of ABS filament reinforced with the short fibers can significantly improve the mechanical properties of 3D-printed devices when the infill angle is oriented along the vector of the applied load. In such a case, the elastic modulus and tensile strength can be increased by more than 1.7 and 1.5 times, respectively. The use of a larger nozzle diameter led to the growth of tensile strength by an average of 12.5%. When the macroscopic load is applied along the normal to the printed layers, the addition of short fibers does not give much gain in mechanical properties compared to pure ABS, which was confirmed by both standard tensile and fracture toughness tests. The surface of the fractured samples was examined using scanning electronic microscopy, which allowed us to make conclusions on the type of defects as well as on the level of adhesion between the polymeric matrix and different types of short fibers.