Copper-Decorated Titanium Electrodes: Impact of Surface Modifications of Substrate on the Morphology and...

This study investigates the effect of surface modifications of the titanium substrate on the growth of electrochemically deposited copper. These materials are intended to serve as cathodes in the electroreduction of nitrates in aqueous solutions. Surface modifications included the use of hydrogen fluoride for titanium etching and anodization to promote the growth of a structured titania nanotube array. The effect of an intermediate calcination step for the nanotubes before deposition was assessed along with a comparison to an untreated substrate electrode. The materials were comprehensively characterized by SEM, XRD, contact angle, potentiodynamic tests, EIS, and cyclic voltammetry. Their electrocatalytic ability was tested in the reduction of aqueous solutions containing nitrates. The results reveal that surface finishing impacted the shape and size of the Cu microparticles, as well as the nucleation mechanism enabling a crystal-facet-controllable synthesis. All the materials exhibited microsized copper particles with a spherical shape with some clusters. On the etched titanium surface, a high number of heterogeneous submicroscopic particles were also present. The thermally treated anodized substrate promoted the development of a combination of sparse microparticles corresponding to defect sites in amorphous titanium and the presence of a diffuse coating of octahedral nanosized particles whose growth was promoted by the tetragonal structure of anatase crystals. Electrochemical tests display reduced charge transfer resistance upon copper deposition on the modified substrates, which is indicative of the enhanced conductivity of the coated materials. Additionally, cyclic voltammetry and electrolysis experiments reveal the electrodes' potential for nitrate reduction, showing a better response for the etched titanium substrate (30% nitrate removal, after 2 h at 25 mA cm^-2).