Analyzing the Surface Topography of Hafnium Nitride Coating on Titanium Screws: An In Vitro Analysis

Background The use of surface coatings to enhance the properties lacking in titanium has attracted significant focus in recent times. Hafnium nitride (HfN) coatings could be explored as promising in the osteoinductive properties of titanium implants. HfN exhibits excellent mechanical attributes, such as hardness and wear resistance, and is often used as a coating on high-end equipment for protection. The findings from this research may carve a new path for the production and optimization of HfN coatings to enhance the longevity and augment properties of implant materials. Thus, the present study was orchestrated to elucidate the surface morphology of HfN coating, ultimately contributing to the advancement of dental implant biomaterials. Materials and methods A total of twenty samples of medical grade commercially pure titanium screws (2 mm diameter and 7 mm length) were procured from G. R. Bioure Surgical System Pvt. Ltd., Ravali, Uttar Pradesh, India, and ten samples were reacted with HfN (0.1 M) (Nano Research Elements, Kurukshetra, Haryana, India) in 100% ethanol and stirred continuously for about 48 hours. Then these screw samples were immersed in the prepared colloidal suspension and sintered for two hours at 400 degrees centigrade. The implant screws were affixed onto metal supports. The magnifications for photomicrographs at ×30, ×200, ×1,500, ×3,000, and ×5,000 were standardized. Elementary semi-quantitative analysis of both dental implants was conducted using energy-dispersive X-ray spectrometry (EDX) coupled with the field emission scanning electron microscope (FE-SEM) equipment (JEOL Ltd., Akishima, Tokyo, Japan). The software used for the analysis of the obtained images is SEM Center. Results The surface analysis using the scanning electron microscope (SEM) showed the coating of HfN over titanium screws. The difference in surface morphology of both the group of implant screws can be visualized under 40.0 and 10.0 mm working distance (WD) for both groups. The surface analysis using the EDX of uncoated titanium screws shows five elements in the spectrum: titanium (Ti), oxygen (O), aluminum (Al), carbon (C), and vanadium (V). The EDX of the HfN-coated screws has two additional metals dispersed in the spectrum, hafnium (Hf). The element characteristics are tabulated with their apparent concentration, k ratio, line type, weight percentage, standard label, and factory label for uncoated titanium screws and HfN-coated titanium screws. Conclusion The study evaluated HfN coating over medical grade commercially pure titanium. The surface topography of coated versus uncoated was visualized. The scanning electron microscope (SEM) images showed a homogenous coating over the titanium surfaces, and the EDX showed elemental dispersion of the coated implant. The study aims to provide a comprehensive understanding of the coating's surface morphology, which will aid in the development of more durable and biocompatible implants. This thereby provides a promising scope for further research of this novel metal coating for use in the biomedical sectors, specifically for dental implants.