Effect of rotation frequency of polishing discs on the surface roughness of resin composite material

The aim of this study was to evaluate the effect of rotation frequency (rpm) of different polishing discs on the surface roughness of a nanohybrid resin composite material. 126 specimens were prepared in metal molds of 10 mm diameter and 2 mm depth using a nanohybrid resin composite material. The prepared specimens were kept in distilled water for 24 hours. Polishing treatments at 5k, 10k, 15k, and 20k rpm were applied to the nanohybrid resin composite material by grouping different brand polishing discs: Sof-Lex Contouring and Polishing Discs (3M Espe, USA) (3M Group), Optidisc (Kerr Corporation, USA) (Kerr Group), Super-Snap Rainbow Technique Kit (Shofu Dental, Japan) (Shofu Group), Finishing Disc (Bisco Dental, USA) (Bisco Group). The surface roughness was evaluated at three different points by atomic force microscopy for all specimens and scanning electron microscopy was used for visual assessment. Data were evaluated by Two Way ANOVA and Tukey's HSD Test. The mean surface roughness (Ra, μm) of all prepared samples showed significant differences (α = 0.05). According to Two-Way ANOVA, there is a statistically significant relationship between the rpm values and the discs. The 3M group showed the highest roughness value at all rpm speeds. Shofu group at 15k, 20k rpm, Bisco group at 10k, 15k, 20k rpm, the Kerr group at 15k, 20k rpm showed the lowest roughness value and had roughness close to the surfaces finished with a mylar strip. The smoothest surfaces were obtained at 15k rpm, even though polishing discs from different brands were used. It was also observed that 5k and 20k rpm polishing speeds can increase the surface roughness of the nanohybrid resin composite material.