CsZnPbBr₃/ZnS core/shell perovskite nanocrystals for stable and efficient white light-emitting diodes

The widespread applicability of perovskite nanocrystals (PeNCs) is impeded by their intrinsic instability. A promising solution is utilizing robust chalcogenides as a protective shell to shield the sensitive luminescent cores from the external environment. However, the inferior structural stability and surface lability of PeNCs usually lead to perovskite phase transition during shell growth. Herein, we introduced smaller Zn ions to partially replace Pb ions in perovskites, which reduces the Pb-X bond length and enhances the Pb-X bond energy for inner lattice stabilization. Simultaneously, extra oleylammonium bromide (OAmBr) was added to protect the labile surface of PeNCs by compensating for the detachment of ligands and the loss of surface Br ions. As a result, the dual strategies enable the epitaxial growth of a ZnS shell and significantly enhance the chemical stability of CsZnPbBr₃/ZnS core/shell PeNCs. After three thermal cycles ranging from 300 to 450 K, the core/shell PeNCs retained 70% of their initial photoluminescence (PL) intensity. In stark contrast, the pristine CsPbBr₃ PeNCs exhibit complete PL quenching after just the first temperature cycle. For practical applications, the green core/shell PeNCs were integrated with commercially available red-emitting phosphors on a blue-emitting InGaN chip to fabricate a white light-emitting diode (WLED), which demonstrates a high luminous efficacy (LE) of 61.3 lm W^-1 and nearly constant Commission Internationale de l'Eclairage (CIE) coordinates under varying operating currents.