Structure Effects on Swelling Properties of Hydrogels Based on Sodium Alginate and Acrylic Polymers
Grzegorz Kowalski1, Mariusz Witczak1, Łukasz Kuterasiński2
1Department of Engineering and Machinery for Food Industry, Faculty of Food Technology, University of Agriculture in Kraków, ul. Balicka 122, 30-149 Kraków, Poland.
Abstract:
Hydrogels based on sodium alginate (SA) and partially neutralised poly(acrylic acid) were obtained by radical polymerisation. The hydrogels were cross-linked with N,N'-methylenebisacrylamide (MBA), simultaneously grafting the resulting polymer onto SA. The findings of the FTIR spectroscopy showed that all of the hydrogels were effectively synthesized and sodium alginate was chemically bonded with the poly(sodium acrylate) matrix. DSC analysis of the melting heat and glass transition parameters indicated that the hydrogel structure had changed as a result of the cross-linking process. Sodium alginate and MBA were tested at different concentrations to determine how they affected the hydrogel properties. A very high content of the biopolymer, i.e., sodium alginate, was used in our research, up to 33 wt%. This resulted in durable and stable hydrogels with a very high ability to uptake water, comparable to hydrogels based on synthetic polymers only. The ability to swell is inversely proportional to the quantity of MBA present. By increasing the amount of sodium alginate in the hydrogel, the ability of the hydrogel to absorb water is reduced. However, water uptake remains relatively high at 350 g·g-1, even for the hydrogel with the highest SA content.
Related Concept Videos
03:05Acid Strength and Molecular Structure
In the absence of any leveling effect, the acid strength of binary compounds of hydrogen with nonmetals (A) increases as the H-A bond strength decreases down a group in the periodic table. For group 17, the order of increasing acidity is HF < HCl < HBr < HI. Likewise, for group 16, the order of increasing acid strength is H2O < H2S < H2Se < H2Te. Across a row in the periodic table, the acid strength of binary hydrogen compounds increases with increasing...
02:34Molecular Structure and Acidity
The size effect explains the change in atomic size on acidity. When comparing the acids formed from elements that belong to the same column in the periodic table, their atomic sizes...
02:11Leveling Effect and Non-Aqueous Acid-Base Solutions
The Leveling Effect of a Solvent
A generic acid (HA) reacts with the generic base (B-) to yield the corresponding conjugate base (A-) and conjugate acid (HB):
01:28Structures of Carboxylic Acid Derivatives
Carboxylic acid derivatives contain an acyl group attached to a heteroatom such as chlorine, oxygen, or nitrogen. The carbonyl carbon and oxygen are both sp2-hybridized with an unhybridized p orbital.
The three sp2 orbitals of the carbonyl carbon form three σ bonds, one each with the carbonyl oxygen, the α carbon, and the heteroatom, whereas the other two sp2 orbitals of the carbonyl oxygen are occupied by the lone pairs. Further, the unhybridized p...
01:21Basicity of Aliphatic Amines
To measure the basicity of amines, two conventions are generally used. The first defines Kb as the basicity constant for the deprotonation reaction of water by the amine, as presented in Figure 1. Conventionally, lower Kb indicates higher...
01:31Physical Properties of Carboxylic Acids