Assessment of the Effect of Surface Modification of Metal Oxides on Silver Nanoparticles: Optical Properties and...

Silver nanoparticles (AgNPs) have garnered significant interest due to their distinctive properties and potential applications. Traditional fabrication methods for nanoparticles often involve high-energy physical conditions and the use of toxic solvents. Various green synthesis approaches have been developed to circumvent these issues and produce environmentally benign nanoparticles. Our study focuses on the green synthesis of AgNPs using L-ascorbic acid and explores the modification of their properties to enhance antibacterial and anticancer effects. This is achieved by coating the nanoparticles with Zinc oxide (ZnO) and Silica oxide (SiO₂), which alters their optical properties in the visible spectrum. The synthesized formulations-AgNPs, zinc oxide-silver nanoparticles (Ag@ZnO), and silica oxide-silver nanoparticles (Ag@SiO₂) core/shell nanoparticles-were characterized using a suite of physicochemical techniques, including Transmission Electron Microscopy (TEM), Dynamic Light Scattering (DLS), Zeta potential measurement, UV-Vis spectroscopy, Refractive Index Measurements, and Optical Anisotropy Assessment. TEM imaging revealed particle sizes of 11 nm for AgNPs, 8 nm for Ag@ZnO, and 400 nm for Ag@SiO₂. The Zeta potential values for Ag@ZnO and Ag@SiO₂ were measured at -17.0 ± 5 mV and -65.0 ± 8 mV, respectively. UV-Vis absorption spectra were recorded for all formulations in the 320 nm to 600 nm wavelength range. The refractive index of AgNPs at 404.7 nm was 1.34572, with slight shifts observed for Ag@ZnO and Ag@SiO₂ to 1.34326 and 1.37378, respectively. The cytotoxicity of the nanocomposites against breast cancer cell lines (MCF-7) was assessed using the MTT assay. The results indicated that AgNPs and Ag@ZnO exhibited potent therapeutic effects, with IC50 values of 494.00 µg/mL and 430.00 µg/mL, respectively, compared to 4247.20 µg/mL for Ag@SiO2. Additionally, the antibacterial efficacy of AgNPs was significantly enhanced under visible light irradiation. Ag@ZnO demonstrated substantial antibacterial activity both with and without light exposure, while the Ag@SiO2 nanocomposites significantly reduced the inherent antibacterial activity of silver. Conversely, the Ag@ZnO nanocomposites displayed pronounced antibacterial and anticancer activities. The findings suggest that silver-based nanocomposites, particularly Ag@ZnO, could be practical tools in water treatment and the pharmaceutical industry due to their enhanced therapeutic properties.