Bone-to-Implant Contact in Implants with Plasma-Treated Nanostructured Calcium-Incorporated Surface (XPEEDActive)...

Titanium implants undergo an aging process through surface hydrocarbon deposition, resulting in decreased wettability and bioactivity. Plasma treatment was shown to significantly reduce surface hydrocarbons, thus improving implant hydrophilicity and enhancing the osseointegration process. This study investigates the effect of plasma surface treatment on bone-to-implant contact (BIC) of implants presenting a nanostructured calcium-incorporated surface (XPEED^®). Following a Randomized Controlled Trial (RCT) design, patients undergoing implant surgery in the posterior maxilla received additional plasma-treated (n = 7) or -untreated (n = 5) 3.5 × 8 mm implants that were retrieved after a 4-week healing period for histological examination. Histomorphometric analysis showed that plasma-treated implants exhibited a 38.7% BIC rate compared to 22.4% of untreated implants (p = 0.002), indicating enhanced osseointegration potential. Histological images also revealed increased bone formation and active osteoblastic activity around plasma-treated implants when compared to untreated specimens. The findings suggest that plasma treatment improves surface hydrophilicity and biological response, facilitating early bone formation around titanium implants. This study underscores the importance of surface modifications in optimizing implant integration and supports the use of plasma treatment to enhance osseointegration, thereby improving clinical outcomes in implant dentistry and offering benefits for immediate and early loading protocols, particularly in soft bone conditions.